Electromagnetic stirring rollers utilize electromagnetic force to induce regular motion in metal melts, necessitating different designs based on the intended purpose and effect. For primary aluminum melting furnaces and holding furnaces, the primary objective is to achieve uniform temperature and composition within a short period of time, requiring **ooth, three-dimensional stirring in all directions. When used for stirring during the melting process of scrap aluminum, the main goals are to facilitate melting at low temperatures and rapid heat exchange, thus promoting a large circulation volume of the metal melt. In this scenario, it is necessary to install the electromagnetic stirrer at a location where the melt is prone to circulation. Regardless of whether it is a square furnace, round furnace, single-chamber furnace, or double-chamber furnace, the installation of inductors can generally be divided into bottom-mounted and side-mounted configurations. The bottom-mounted installation is primarily used for new furnaces or furnaces where the height of the melt pool varies during production. This configuration achieves better stirring effects and is less affected by changes in the height of the melt pool. In scrap aluminum recycling furnaces, the installation location should be offset from the center of the furnace.
连铸
|
|
辊装部位
|
辊名称
|
堆焊材料型号
|
硬度HRC
|
使用效果比较
|
结晶器
|
足辊
|
WLDC900
|
36-40
|
寿命高达过钢量100万吨
|
0段前部
|
分节小辊
|
WLDC900
|
36-40
|
寿命高达过钢量100万吨
|
0段上部
|
分节小辊
|
WLDC2000
|
44-46
|
过钢量达150万吨
|
弯曲段
|
直径小于等于150
|
WLDC3系列
|
40-42
|
过钢量达150万吨
|
扇形段
|
直径150~180 WLDC3系列
|
WLDC3系列
|
42-43
|
过钢量达200万吨
|
矫直段
|
直径180~200 WLDC3系列
|
WLDC3系列
|
45-47
|
过钢量达200万吨
|
水平段
|
直径200~350 WLDC3系列
|
WLDC3系列
|
47-48
|
过钢量达大于300万吨
|
热轧 冷轧
|
|
辊装部位
|
辊名称
|
推荐堆焊材料
|
硬度 HRc
|
效果比较
|
初轧机架
|
辊道辊
|
WLDC2000
|
45~48
|
寿命比喷焊WC辊提高1倍
|
初轧机架
|
工作辊
|
WLDC 4
|
55~58
|
寿命提高
|
初轧机架
|
支撑辊
|
WLDC 4
|
56~58
|
寿命提高
|
除鳞机架
|
除鳞辊
|
WLDC8&12
|
52~54
|
寿命提高1倍
|
精轧机架
|
活套辊
|
WLDC8
|
52~54
|
寿命提高4倍
|
输出辊道
|
轧边辊
|
WLDC 4&17
|
48~50
|
寿命提高4倍
|
输出辊道
|
辊道辊
|
WLDC8
|
54~56
|
提高4倍，过钢百万吨/0.3mm
|
输出辊道
|
夹送辊
|
WLDC 4&17
|
50~52
|
寿命提高4倍
|
卷取机架
|
助卷辊
|
WLDC17&8
|
52~58
|
寿命比喷焊辊提高近一倍
|
卷取机架
|
涨力辊
|
WLDC 4&8
|
50~54
|
比喷焊提高1倍，26万吨/次
|
卷取输送
|
卷取辊
|
WLDC 4&17
|
54~58
|
比喷焊提高1倍，26万吨/次
|
冷轧酸洗
|
支撑辊
|
WLDC 4
|
50~55
|
使用寿命明显提高
|
冷轧酸洗
|
除鳞辊
|
WLDC 4
|
50~55
|
使用寿命明显提高
|
冷轧酸洗
|
夹送辊
|
WLDC 4
|
50~55
|
使用寿命明显提高
|
冷轧酸洗
|
矫直辊
|
WLDC 4
|
50~55
|
使用寿命明显提高
|
中厚板 初轧机
|
|
辊装部位
|
辊名称
|
推荐堆焊材料
|
硬度HRc
|
效果比较
|
输送辊道
|
辊道辊
|
WLDC2000
|
45~48
|
寿命比喷焊WC 辊提高1倍
|
输出辊道
|
转向辊
|
WLDC8/12
|
52~54
|
寿命提高1倍
|
热矫直机
|
工作辊
|
WLDC8
|
52~54
|
寿命提高4倍
|
冷矫直机
|
工作辊
|
WLD**
|
55~57
|
寿命提高4倍
|
轧机
|
支撑辊
|
WLD**
|
50~52
|
寿命提高4倍
|
安装部位
|
轧辊名称
|
堆焊材料型号
|
硬度HRc
|
使用效果比较
|
轧钢机架
|
初轧轧辊
|
Weldclad1，4
|
33—54
|
比合金新辊高2倍
|
中型轧机
|
型钢轧辊
|
Weldclad4，17
|
50—58
|
比合金新辊高3倍
|
大型轧机
|
型钢轧辊
|
Weldclad4，17
|
50—58
|
比合金新辊高4倍
|
型钢轧机
|
重轨轧辊
|
Weldclad4，17
|
50—58
|
比合金新辊高3倍
|
型钢轧机
|
立桩轧辊
|
Weldclad4，8
|
45—54
|
比合金新辊高2倍
|
常耗备件
|
|
设备名称
|
备件名称
|
推荐堆焊材料
|
硬度HRc
|
使用效果比较
|
轧钢机架
|
轴承箱
|
WLDC11、12
|
30～43
|
使用寿命提高3倍
|
支撑辊
|
辊颈
|
WLDC 4、8
|
45～54
|
使用寿命有所提高
|
高炉炉顶
|
溜槽
|
CC187TiC
|
57～60
|
使用寿命提高2倍
|
高炉
|
料斗
|
C**5
|
58～64
|
使用寿命提高2倍
|
烧结机
|
箅板、筛板
|
C**5
|
58～64
|
使用寿命提高1倍
|
烧结***
|
单齿辊
|
C**5
|
58～64
|
使用寿命提高1倍
|
磨煤机
|
对辊
|
CC31
|
58～64
|
使用寿命提高3倍
|
引定杆
|
夹头
|
CS400
|
32～45
|
使用寿命提高2倍
|
钢水包
|
耳轴
|
CS300
|
25～34
|
使用寿命提高3倍
|
轧机
|
剪刀
|
CS400
|
32～45
|
使用寿命提高2倍
|
主轧钢机
|
联结轴
|
WLDC11、12
|
26～35
|
使用寿命提高1倍
|
主轧钢机
|
联轴器
|
WLDC11、12
|
26～35
|
使用寿命提高1倍
|
轧机牌坊
|
侧滑动导板
|
WLDC11、12
|
39～40
|
使用寿命提高2倍
|
起重天车
|
吊车轮
|
WLDC11/10
|
26～30
|
节省60%，不伤轨道
|
液压缸
|
活塞杆
|
WLDC6
|
40～46
|
高1倍、镀层不脱落
|