Application of su***cing technology in hot strip mills
Hot-rolled strip conveyor rolls, descaler rolls, supports and roll necks of finishing mill stands, loop rolls, edging rolls of output roller tables, pinch rolls, wrapper rolls of coiler stands, and tension rolls are not only subject to intense thermal wear but also endure adverse working conditions such as thermal fatigue, wear, adhesion nodules, cavitation, and scratches from iron scale. The severe damage and scratches on the product su***ce require frequent grinding of the roll su***ce, which greatly affects production efficiency and product quality.
By applying WELDCLAD su***cing technology to the aforementioned frequently worn rollers, a high-carbon chromium alloy with high wear resistance, corrosion resistance, and thermal fatigue resistance can be deposited, significantly enhancing the service life of various rollers. This process can also eliminate or reduce adhesion, nodules, and severe scratches, maintaining the roller profile and su***ce finish, improving corrosion resistance, and facilitating the improvement of strip steel quality, production efficiency, and production costs. This creates substantial economic benefits for steel mills.
连铸
|
|
辊装部位
|
辊名称
|
堆焊材料型号
|
硬度HRC
|
使用效果比较
|
结晶器
|
足辊
|
WLDC900
|
36-40
|
寿命高达过钢量100万吨
|
0段前部
|
分节小辊
|
WLDC900
|
36-40
|
寿命高达过钢量100万吨
|
0段上部
|
分节小辊
|
WLDC2000
|
44-46
|
过钢量达150万吨
|
弯曲段
|
直径小于等于150
|
WLDC3系列
|
40-42
|
过钢量达150万吨
|
扇形段
|
直径150~180 WLDC3系列
|
WLDC3系列
|
42-43
|
过钢量达200万吨
|
矫直段
|
直径180~200 WLDC3系列
|
WLDC3系列
|
45-47
|
过钢量达200万吨
|
水平段
|
直径200~350 WLDC3系列
|
WLDC3系列
|
47-48
|
过钢量达大于300万吨
|
热轧 冷轧
|
|
辊装部位
|
辊名称
|
推荐堆焊材料
|
硬度 HRc
|
效果比较
|
初轧机架
|
辊道辊
|
WLDC2000
|
45~48
|
寿命比喷焊WC辊提高1倍
|
初轧机架
|
工作辊
|
WLDC 4
|
55~58
|
寿命提高
|
初轧机架
|
支撑辊
|
WLDC 4
|
56~58
|
寿命提高
|
除鳞机架
|
除鳞辊
|
WLDC8&12
|
52~54
|
寿命提高1倍
|
精轧机架
|
活套辊
|
WLDC8
|
52~54
|
寿命提高4倍
|
输出辊道
|
轧边辊
|
WLDC 4&17
|
48~50
|
寿命提高4倍
|
输出辊道
|
辊道辊
|
WLDC8
|
54~56
|
提高4倍，过钢百万吨/0.3mm
|
输出辊道
|
夹送辊
|
WLDC 4&17
|
50~52
|
寿命提高4倍
|
卷取机架
|
助卷辊
|
WLDC17&8
|
52~58
|
寿命比喷焊辊提高近一倍
|
卷取机架
|
涨力辊
|
WLDC 4&8
|
50~54
|
比喷焊提高1倍，26万吨/次
|
卷取输送
|
卷取辊
|
WLDC 4&17
|
54~58
|
比喷焊提高1倍，26万吨/次
|
冷轧酸洗
|
支撑辊
|
WLDC 4
|
50~55
|
使用寿命明显提高
|
冷轧酸洗
|
除鳞辊
|
WLDC 4
|
50~55
|
使用寿命明显提高
|
冷轧酸洗
|
夹送辊
|
WLDC 4
|
50~55
|
使用寿命明显提高
|
冷轧酸洗
|
矫直辊
|
WLDC 4
|
50~55
|
使用寿命明显提高
|
中厚板 初轧机
|
|
辊装部位
|
辊名称
|
推荐堆焊材料
|
硬度HRc
|
效果比较
|
输送辊道
|
辊道辊
|
WLDC2000
|
45~48
|
寿命比喷焊WC 辊提高1倍
|
输出辊道
|
转向辊
|
WLDC8/12
|
52~54
|
寿命提高1倍
|
热矫直机
|
工作辊
|
WLDC8
|
52~54
|
寿命提高4倍
|
冷矫直机
|
工作辊
|
WLD**
|
55~57
|
寿命提高4倍
|
轧机
|
支撑辊
|
WLD**
|
50~52
|
寿命提高4倍
|
安装部位
|
轧辊名称
|
堆焊材料型号
|
硬度HRc
|
使用效果比较
|
轧钢机架
|
初轧轧辊
|
Weldclad1，4
|
33—54
|
比合金新辊高2倍
|
中型轧机
|
型钢轧辊
|
Weldclad4，17
|
50—58
|
比合金新辊高3倍
|
大型轧机
|
型钢轧辊
|
Weldclad4，17
|
50—58
|
比合金新辊高4倍
|
型钢轧机
|
重轨轧辊
|
Weldclad4，17
|
50—58
|
比合金新辊高3倍
|
型钢轧机
|
立桩轧辊
|
Weldclad4，8
|
45—54
|
比合金新辊高2倍
|
常耗备件
|
|
设备名称
|
备件名称
|
推荐堆焊材料
|
硬度HRc
|
使用效果比较
|
轧钢机架
|
轴承箱
|
WLDC11、12
|
30～43
|
使用寿命提高3倍
|
支撑辊
|
辊颈
|
WLDC 4、8
|
45～54
|
使用寿命有所提高
|
高炉炉顶
|
溜槽
|
CC187TiC
|
57～60
|
使用寿命提高2倍
|
高炉
|
料斗
|
C**5
|
58～64
|
使用寿命提高2倍
|
烧结机
|
箅板、筛板
|
C**5
|
58～64
|
使用寿命提高1倍
|
烧结***
|
单齿辊
|
C**5
|
58～64
|
使用寿命提高1倍
|
磨煤机
|
对辊
|
CC31
|
58～64
|
使用寿命提高3倍
|
引定杆
|
夹头
|
CS400
|
32～45
|
使用寿命提高2倍
|
钢水包
|
耳轴
|
CS300
|
25～34
|
使用寿命提高3倍
|
轧机
|
剪刀
|
CS400
|
32～45
|
使用寿命提高2倍
|
主轧钢机
|
联结轴
|
WLDC11、12
|
26～35
|
使用寿命提高1倍
|
主轧钢机
|
联轴器
|
WLDC11、12
|
26～35
|
使用寿命提高1倍
|
轧机牌坊
|
侧滑动导板
|
WLDC11、12
|
39～40
|
使用寿命提高2倍
|
起重天车
|
吊车轮
|
WLDC11/10
|
26～30
|
节省60%，不伤轨道
|
液压缸
|
活塞杆
|
WLDC6
|
40～46
|
高1倍、镀层不脱落
|